PITT-CHAR XP
Epoxy Intumescent Coating
- Superior fir & corrosion protection
- Unique flexibility
- Superior mechanical resistance
- Suitable for cryogenic exposure
- Complies with international fire standards
Volume Solids% (ISO 3233) |
100 |
Dry Film Thickness (µm) |
dependent |
Theoretical Coverage (m²/l) |
0.25 (at 5mm/0.2) |
Mixing Ratio (Volume) |
2.33:1 |
Packing Size (kg) |
70 |
Thinner /Cleaner |
Thinner T-47/Amercoat 920 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |
STEELGUARD FM 549
Thin Film Intumescent Coating
- Thin film solvent based intumescent
- Tested to international fire test standards
- Up to 2 hours fire protection of structural steel
- Off-site or on-site application
- Up to 1.5 mm dry film thickness application in a single coat
- Rapid job completion
- For use in C1 & C2 internal environments - no sealer coat required for dry internal C1 service conditions ( ISO 12944)
Volume Solids% (ISO 3233) |
68 +-3 |
Dry Film Thickness (µm) |
250 - 1500 |
Theoretical Coverage (m²/l) |
2.72 (250 µm) 0.45 (1500 µm) |
Mixing Ratio (Volume) |
|
Packing Size (ltr) |
20 |
Thinner /Cleaner |
Amercoat 65 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |
STEELGUARD FM 550
Thin Film Intumescent Coating
- Thin film solvent based intumescent
- Tested to international fire test standards
- Up to 2 hours fire protection of structural steel
- Off-site or on-site application
- Up to 1.5 mm dry film thickness application in a single coat
- Rapid job completion
- For use in C1,C2,C3 & C2 internal environments - no sealer coat required for dry internal C1 service conditions ( ISO 12944)
Volume Solids% (ISO 3233) |
68 +-3 |
Dry Film Thickness (µm) |
250 - 1500 |
Theoretical Coverage (m²/l) |
2.72 (250 µm) 0.45 (1500 µm) |
Mixing Ratio (Volume) |
|
Packing Size (ltr) |
20 |
Thinner /Cleaner |
Amercoat 65 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |
STEELGUARD 560
Thin Film Intumescent Coating
- Fast drying solvent based thin film intumescent
- Rapid drying providing reduced times to handling
- Tested to internal fire test standards
- Up to 2 hours fire protection of structural steel
- Off-site or on-site application
- Up to 1.0 mm dry film thickness application in a single coat
- For use in C1,C2,C3 & C2 internal environments - no sealer coat required for dry internal C1 service conditions ( ISO 12944)
Volume Solids% (ISO 3233) |
68 +-3 |
Dry Film Thickness (µm) |
250 - 1000 |
Theoretical Coverage (m²/l) |
2.72 (250 µm) 0..68 (1000 µm) |
Mixing Ratio (Volume) |
|
Packing Size (ltr) |
20 |
Thinner /Cleaner |
Amercoat 65 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |
STEELGUARD 564
Thin Film Intumescent Coating
- Fast drying solvent based thin film intumescent
- Rapid drying providing reduced times to handling
- 120 minute fire protection on structural I beams
- Off-site or on-site application
- Up to 1.0 mm dry film thickness application in a single coat
- For use in C1,C2,C3 & C2 internal environments - no sealer coat required for dry internal C1 service conditions ( ISO 12944)
Volume Solids% (ISO 3233) |
75 +-3 |
Dry Film Thickness (µm) |
200 - 1000 |
Theoretical Coverage (m²/l) |
1.07 (700 µm) |
Mixing Ratio (Volume) |
|
Packing Size (ltr) |
20 |
Thinner /Cleaner |
Amercoat 65 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |
STEELGUARD 2458
Single Pack Acrylic Finish
- EPA compliant (1998) as a finish for Steelguard Intumescent coatings
- High build
- Suitable for external exposure
- Single pack material
- Good colour retention
Volume Solids% (ISO 3233) |
45 +- 2 |
Dry Film Thickness (µm) |
50 - 125 |
Theoretical Coverage (m²/l) |
6.0 (75 µm) |
Mixing Ratio (Volume) |
|
Packing Size (ltr) |
20 |
Thinner /Cleaner |
Amercoat 65 |
Data Sheets |
Technical Data |
|
MSDS Resin | MSDS Cure |